Polyvinyl butyral - epoxy-resin based, two component, reaction-dry, anti-corrosive pigments containing anticorrosive primer to protect steel, aluminum and galvanized surfaces against corrosion, and to increase the adhesion of the top coat paints to be applied.

Surface Preparation&Application
Surfaces should be cleaned of old paint film, oil, dust, dirt, moist, chloride, sulphate salts, rust, rolled mud, tempering, casting - welding burrs etc. which will reduce adhesion on the application surface . Bevel the 90° sharp corners and edges of the application surface and send the surface at minimum Sa2 ½ (ISO 8501-1, SSPC-SP10) degrees, (sand - grid scraper) and prime the scraped surface in 1 to 2 hours with Wash Primer. After the primer has hard dried (in 4 to 6 hours), the top coat paint can be applied. Mix the primer and the hardener in the given ratio until a homogeneous mixture is obtained. Rest the mixture for 2 to 3 minutes for preliminary reaction and apply with the recommended apparatuses. Continue stirring to prevent settling during longtime applications. The surface temperature must be minimum 3 Celsius degrees higher than the dew temperature. Application at temperatures near the dew point is not recommended. For the topcoat application wait for 24 hours between coats. Application Temperature: Min. +10°C / Max. + 30°C

Thinning / Blending Ratio
2A / 1B - Epoxy Thinner 5- 10% by weight

Coverage Area
12-13 m²/L; 11-12 m²/kg (15 - 20 µ DFT)

Drying Time
Touch dry in 20-30 minutes and hard dry in 24 hours.

Recommended Application Tools
Air - airless spray

Package
15 kg Set (10 kg A + 5 kg B)